Avaliação do efeito de parâmetros reacionais sobre o comportamento fototérmico

Metadados Descrição Idioma Autor(es): dc.contributor Paterno, Leonardo Giordano – Autor(es): dc.creator Moreira, Caio César Coradi – Information de aceite: dc.date.accessioned 2021-10-14T18:53:08Z – Information de disponibilização: dc.date.accessible 2021-10-14T18:53:08Z – Information de envio: dc.date.issued 2019-03-06 – Information de envio: dc.date.issued 2019-03-06 – Information de envio: dc.date.issued 2019-03-06 – Information de envio: dc.date.issued 2018-08-29 – Fonte completa do materials: dc.identifier http://repositorio.unb.br/deal with/10482/34100 – Fonte: dc.identifier.uri http://educapes.capes.gov.br/deal with/capes/642239 – Descrição: dc.description Dissertação (mestrado)—Universidade de Brasília, Instituto de Química, Programa de Pós-Graduação em Química, 2018. – Descrição: dc.description O objetivo deste trabalho foi analisar os efeitos de parâmetros reacionais sobre a estrutura
e o comportamento fototérmico de amostras de óxido de grafeno (OG), preparadas por
rotas distintas de oxidação do grafite e de esfoliação do óxido de grafite (OGR). Para
tanto, foram avaliadas as amostras obtidas pelo método de Hummers, com e sem préoxidação,
e tempos variados de esfoliação com ultrassom de alta potência. Além disso,
algumas amostras foram submetidas à reação de carboxilação, com o intuito de diminuir
ainda mais o tamanho das folhas de OG. A partir de dados de espectroscopia no
infravermelho com transformada de Fourier no modo de refletância complete atenuada (FTIRATR),
observa-se que as amostras mais oxidadas são aquelas obtidas após duas oxidações
sucessivas do grafite, apenas pelo método de Hummers, e sem pré-oxidação. Entretanto,
não se verifica uma correlação direta entre o diâmetro hidrodinâmico das amostras
(medido por espalhamento dinâmico de luz) e o tempo de tratamento em ultrassom. As
amostras obtidas em diferentes condições apresentam diâmetros variando entre 140 nm e
650 nm. A caracterização das amostras por espectroscopia micro Raman revela que o
tamanho de cristalito e a distância entre os defeitos estruturais diminuem à medida que o
grafite é oxidado e depois esfoliado até OG. Os espectros de absorção UV-vis das
suspensões aquosas de OG apresentam as transições n®p* e p®p* esperadas para a
estrutura de grafite oxidado, com coeficientes de absortividade óptica (e) entre 9 e 118
L.g-1.cm-1. Foi observado que o efeito fototérmico das amostras de OG é proveniente da
combinação de dois fatores principais: estrutura molecular e tamanho das folhas. No
geral, nota-se que as amostras com os maiores valores de e e λmáx possuem maior absorção
no infravermelho próximo. Consequentemente, são as amostras que apresentam maior
efeito fototérmico sob irradiação 808 nm e fluência de 230 ± 0,5 mW.cm-2.
Em specific, uma amostra de OG carboxilada, com diâmetro hidrodinâmico de 358 nm
e e = 118 L.g-1.cm-1, exibiu uma variação de temperatura de 50,85oC e atingiu o máximo
de 80oC num intervalo de 12 min. de irradiação. O desempenho observado é superior ao
encontrado na literatura para amostras com características similares e apontam seu
potencial para aplicação em terapia fototérmica. – Descrição: dc.description Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq). – Descrição: dc.description The purpose of this work is to research the results of response parameters on the construction and
photothermal habits of graphene oxide (GO) samples ready underneath totally different
oxidation routes of graphite and exfoliation of the obtained graphitic oxide (GRO). For
this goal, samples are ready by the Hummers technique, with and with out preoxidation
step, and totally different time intervals of excessive energy ultrassound exfoliation. In addition to,
some pattern are submitted to carboxylation response to lower additional the dimensions of GO
sheets. Information from Fourier remodel infrared spectroscopy with attenuated complete
reflectance counsel that essentially the most oxidized samples are these obtained after two
consecutive oxidations of graphite, solely by the Hummers technique and with out preoxidation.
Nonetheless, it isn’t noticed an easy correlation between the
samples hydrodynamic diameter (measured by dynamic gentle scattering) and size of the
ultrasound therapy. Samples ready underneath totally different circumstances exhibit diameters that
span from 140 nm to 650 nm. Characterization carried out by micro Raman spectroscopy
reveals that the crystallite measurement and distance between structural defects lower as
graphite is oxidized and aftewards exfoliated to GO. UV-vis absorption spectra of GO
aqueous suspensions present the n®p* a p®p* transitions, that are anticipated for an
oxidized graphite construction, with optical absorption coefficients (e) between 9 and 118
L.g-1.cm-1. It was noticed that the photothermal impact of OG samples comes from the
mixture of two predominant elements: morphology and molecular construction. Normally, it’s
noticed that samples with greater values of e and λmáx have greater absorption within the close to
infrared. Consequently, these are the samples that present essentially the most vital photothermal
impact underneath 808 nm irradiation and fluency of 230 ± 0,5 mW.cm-2.
Specifically, a carboxylated GO pattern, with a hydrodynamic diameter of 358 nm and
e=118 L.g-1.cm-1, reveals a temperature variation of fifty,85oC and reaches a most of
80oC after 12 min. of irradiation. The efficiency is superior to that discovered within the
literature for samples with related structural options. This commentary factors out their
potential for software in photothermal remedy. – Formato: dc.format software/pdf – Direitos: dc.rights Acesso Aberto – Direitos: dc.rights A concessão da licença deste merchandise refere-se ao termo de autorização impresso assinado pelo autor com as seguintes condições: Na qualidade de titular dos direitos de autor da publicação, autorizo a Universidade de Brasília e o IBICT a disponibilizar por meio dos websites www.bce.unb.br, www.ibict.br, http://hercules.vtls.com/cgi-bin/ndltd/chameleon?lng=pt&pores and skin=ndltd sem ressarcimento dos direitos autorais, de acordo com a Lei nº 9610/98, o texto integral da obra disponibilizada, conforme permissões assinaladas, para fins de leitura, impressão e/ou obtain, a título de divulgação da produção científica brasileira, a partir desta information. – Palavras-chave: dc.topic Óxido de grafeno – Palavras-chave: dc.topic Terapia fotodinâmica – Palavras-chave: dc.topic Oxidação de Hummers Offeman – Título: dc.title Avaliação do efeito de parâmetros reacionais sobre o comportamento fototérmico do óxido de grafeno – Tipo de arquivo: dc.sort livro digital – Aparece nas coleções: UNB